Obere dayameta 225mm Furnace Graphite Electrodes na-eji maka nrụpụta Carborundum na-anụcha ọkụ eletrik
Nka nka
Chart 1: Nka nka Maka Obere Okirikiri Graphite Electrode
| Dayameta | Akụkụ | Nguzogide | Ike Flexural | Modul na-eto eto | Njupụta | CTE | Ash | |
| Inch | mm | μΩ·m | MPa | GPA | g/cm3 | ×10-6/ ℃ | % | |
| 3 | 75 | Electrode | 7.5-8.5 | ≥9.0 | ≤9.3 | 1.55-1.64 | ≤2.4 | ≤0.3 |
| Ọnụ ara | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 4 | 100 | Electrode | 7.5-8.5 | ≥9.0 | ≤9.3 | 1.55-1.64 | ≤2.4 | ≤0.3 |
| Ọnụ ara | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 6 | 150 | Electrode | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Ọnụ ara | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 8 | 200 | Electrode | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Ọnụ ara | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 9 | 225 | Electrode | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Ọnụ ara | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 10 | 250 | Electrode | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Ọnụ ara | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
Chart 2: Ikike ibu ugbu a maka Obere dayameta Graphite Electrode
| Dayameta | Ibu dị ugbu a | Njupụta dị ugbu a | Dayameta | Ibu dị ugbu a | Njupụta dị ugbu a | ||
| Inch | mm | A | A/m2 | Inch | mm | A | A/m2 |
| 3 | 75 | 1000-1400 | 22-31 | 6 | 150 | 3000-4500 | 16-25 |
| 4 | 100 | 1500-2400 | 19-30 | 8 | 200 | 5000-6900 | 15-21 |
| 5 | 130 | 2200-3400 | 17-26 | 10 | 250 | 7000-10000 | 14-20 |
Chart 3: Ogo Electrode Graphite & Nkwenye Maka Obere Dayameta Graphite Electrode
| Ọnụ ala dayameta | Oke dayameta (mm) | Ogologo aha aha | Ndidi | |||
| Inch | mm | Oke. | Min. | mm | Inch | mm |
| 3 | 75 | 77 | 74 | 1000 | 40 | -75-50 |
| 4 | 100 | 102 | 99 | 1200 | 48 | -75-50 |
| 6 | 150 | 154 | 151 | 1600 | 60 | ±100 |
| 8 | 200 | 204 | 201 | 1600 | 60 | ±100 |
| 9 | 225 | 230 | 226 | 1600/1800 | 60/72 | ±100 |
| 10 | 250 | 256 | 252 | 1600/1800 | 60/72 | ±100 |
Atụmatụ Electrodes graphite pere mpe
1.kọmpat nha
2.Superior Heat Resistance
3.Excelent Conductivity
4.Short Preheating Time
Ngwa isi
- Calcium carbide na-agbaze
- Mmepụta Carborund
- Nnụcha corundum
- Ọla na-adịghị ahụkebe na-agbaze
- Ferrosilicon osisi refractory
Uru Gufan
Eletrọd graphite pere mpe anyị na-agbanwegharị ụlọ ọrụ na-agbaze.Nha ha dị kọmpat, nguzogide okpomọkụ dị elu, ezigbo conductivity, na ịdị iche iche na-eme ka ha dabara nke ọma maka ịrụ ọrụ mgbaze.Site n'ịdịte aka ha, ịdị n'otu, oge ikpo ọkụ ngwa ngwa na ike ike, electrodes anyị na-ahụ maka usoro ịgbaze nke ọma ma dị irè, na-enyere gị aka nweta nsonaazụ kacha mma na arụmọrụ gị.Họrọ obere elektrọd graphite dayameta anyị wee hụ ihe dị iche na ọrụ mgbaze gị.